Organic thin film transistors

ABSTRACT

A thin film transistor having an improved gate dielectric layer is disclosed. The gate dielectric layer comprises a poly(4-vinylphenol-co-acrylonitrile) based polymer. The resulting gate dielectric layer has a high dielectric constant and can be crosslinked. Higher gate dielectric layer thicknesses can be used to prevent current leakage while still having a large capacitance for low operating voltages. Methods for producing such gate dielectric layers and/or thin film transistors comprising the same are also disclosed.

BACKGROUND

The present disclosure relates, in various embodiments, to thin-film transistors (TFTs) and/or other electronic devices comprising a semiconducting layer and a gate dielectric layer. The gate dielectric layer comprises a poly(4-vinylphenol-co-acrylonitrile) (PVPA) based polymer. The resulting dielectric layer has a high dielectric constant and can be crosslinked. Certain gate dielectric layer thicknesses can therefore still prevent current leakage while having a large capacitance, enabling low operating voltages.

TFTs are generally composed of, on a substrate, an electrically conductive gate electrode, source and drain electrodes, an electrically insulating gate dielectric layer which separate the gate electrode from the source and drain electrodes, and a semiconducting layer which is in contact with the gate dielectric layer and bridges the source and drain electrodes. Their performance can be determined by the field effect mobility and the current on/off ratio. High mobility and high on/off ratio are desired.

There is interest in organic thin film transistors (OTFTs) for applications such as radio frequency identification (RFID) tags and backplane switching circuits for displays, such as signage, readers, and liquid crystal displays, where high switching speeds and/or high density are not essential. OTFTs may be made using low-cost solution or liquid fabrication techniques. They also have attractive mechanical properties such as being physically compact, lightweight, and flexible.

Recently, there has been an increased interest in organic thin film transistors which can potentially be fabricated using solution-based patterning and deposition techniques, such as spin coating, solution casting, dip coating, stencil/screen printing, flexography, gravure, offset printing, ink jet-printing, micro-contact printing, and the like, or a combination of these processes. Such processes are generally simpler and more cost effective compared to the complex photolithographic processes used in fabricating silicon-based thin film transistor circuits for electronic devices. To enable the use of these solution-based processes in fabricating thin film transistor circuits, solution processable materials are therefore required.

In this regard, gate dielectric layers may be formed by these solution-based processes. However, the gate dielectric layer so formed should be free of pinholes and possess low surface roughness (or high surface smoothness), low leakage current, a high dielectric constant, a high breakdown voltage, adhere well to the gate electrode, be stable in solution at room temperature, and offer other functionality. It should also be compatible with semiconductor materials because the interface between the dielectric layer and the organic semiconductor layer critically affects the performance of the TFT.

Most solution processable polymers used in gate dielectric layers usually have low dielectric constants and do not contain crosslinkable functional groups, so a considerable dielectric thickness is required to reduce gate leakage current to an acceptable level. As a result, the capacitance of the dielectric layer is usually low, leading to high operating voltage and low mobility. Therefore, there is a need of solution processable polymers with high dielectric constant, crosslinkable functional groups, as well as gate dielectric layers formed by such polymers having a certain thickness, high dielectric constant, and high capacitance.

BRIEF DESCRIPTION

The present application discloses, in various exemplary embodiments, dielectric layers and thin film transistors, particularly organic thin film transistors (OTFTs), formed with such layers. The dielectric layers comprise a poly(4-vinylphenol-co-acrylonitrile) based polymer, such as a poly(4-vinylphenol-co-acrylonitrile) copolymer.

In embodiments, a thin film transistor comprising a substrate, a gate dielectric layer, and a semiconducting layer is disclosed, wherein the gate dielectric layer comprises a poly(4-vinylphenol-co-acrylonitrile) based polymer. The polymer may have a dielectric constant of from about 3 to about 18, including from about 4 to about 10.

The poly(4-vinylphenol-co-acrylonitrile) based polymer may be crosslinked. The crosslinking agent can be selected from the group consisting of isocyanates, tri(2-aminoethyl)amine, diethylene triamine, melamine-formaldehyde resins, compounds containing at least two epoxy groups, compounds containing at least two carboxylic acid groups, and acid anhydrides of carboxylic acid, and mixtures thereof.

The molar ratio of 4-vinylphenol to acrylonitrile in the poly(4-vinylphenol-co-acrylonitrile) based polymer may be from about 9:1 to about 1:9, including from about 2:1 to about 1:2.

The gate dielectric layer may further comprise inorganic nanoparticles and/or have a thickness of 2 microns or less.

The semiconducting layer may comprise a polythiophene having the structure of formula (1):

where R and R′ are independently selected from hydrogen, halogen, alkyl, alkoxyalkyl, siloxyalkyl, and perfluoroalkyl; M is a divalent linkage; and n is the number of repeat units.

In specific embodiments, the gate dielectric layer has a thickness of from about 100 nanometers to about 500 nanometers, and a capacitance greater than 5 nF/cm².

In additional embodiments, a gate dielectric layer for an electronic device comprises a poly(4-vinylphenol-co-acrylonitrile) based polymer.

In other embodiments, a method for preparing a thin-film transistor is disclosed, the method comprising:

-   -   providing a substrate, a gate electrode, a gate dielectric         layer, a source electrode, a drain electrode, and a         semiconducting layer, wherein the gate dielectric layer         comprises a poly(4-vinylphenol-co-acrylonitrile) based polymer;     -   wherein the gate dielectric layer separates the gate electrode         from the semiconducting layer, the source electrode, and the         drain electrode.

These and other non-limiting characteristics of the disclosure are more particularly disclosed below.

BRIEF DESCRIPTION OF THE DRAWINGS

The following is a brief description of the drawings, which are presented for the purposes of illustrating the exemplary embodiments disclosed herein and not for the purposes of limiting the same.

FIG. 1 represents a first embodiment of a TFT according to the present disclosure.

FIG. 2 represents a second embodiment of a TFT according to the present disclosure.

FIG. 3 represents a third embodiment of a TFT according to the present disclosure.

FIG. 4 represents a fourth embodiment of a TFT according to the present disclosure.

DETAILED DESCRIPTION

A more complete understanding of the components, processes and apparatuses disclosed herein can be obtained by reference to the accompanying drawings. These figures are merely schematic representations based on convenience and the ease of demonstrating the present disclosure, and are, therefore, not intended to indicate relative size and dimensions of the devices or components thereof and/or to define or limit the scope of the exemplary embodiments.

Although specific terms are used in the following description for the sake of clarity, these terms are intended to refer only to the particular structure of the embodiments selected for illustration in the drawings, and are not intended to define or limit the scope of the disclosure. In the drawings and the following description below, it is to be understood that like numeric designations refer to components of like function.

FIG. 1 illustrates a bottom-gate bottom-contact TFT configuration according to the present disclosure. The TFT 10 comprises a substrate 20 in contact with the gate electrode 30 and a gate dielectric layer 40. Although here the gate electrode 30 is depicted within the substrate 20, this is not required. However, it is important that the gate dielectric layer 40 separates the gate electrode 30 from the source electrode 50, drain electrode 60, and the semiconducting layer 70. The semiconducting layer 70 runs over and between the source and drain electrodes 50 and 60. The semiconductor has a channel length 80 between the source and drain electrodes 50 and 60.

FIG. 2 illustrates another bottom-gate top-contact TFT configuration according to the present disclosure. The TFT 10 comprises a substrate 20 in contact with the gate electrode 30 and a gate dielectric layer 40. The semiconducting layer 70 is placed on top of the gate dielectric layer 40 and separates it from the source and drain electrodes 50 and 60.

FIG. 3 illustrates a bottom-gate bottom-contact TFT configuration according to the present disclosure. The TFT 10 comprises a substrate 20 which also acts as the gate electrode and is in contact with a gate dielectric layer 40. The source electrode 50, drain electrode 60, and semiconducting layer 70 are located atop the gate dielectric layer 50.

FIG. 4 illustrates a top-gate top-contact TFT configuration according to the present disclosure. The TFT 10 comprises a substrate 20 in contact with the source electrode 50, drain electrode 60, and the semiconducting layer 70. The semiconducting layer 70 runs over and between the source and drain electrodes 50 and 60. The gate dielectric layer 40 is on top of the semiconducting layer 70. The gate electrode 30 is on top of the gate dielectric layer 40 and does not contact the semiconducting layer 70.

The gate dielectric layer of the present disclosure comprises a poly(4-vinylphenol-co-acrylonitrile) (“PVPA”) based polymer. The PVPA based polymer contains repeating units derived from at least two monomers, 4-vinylphenol and acrylonitrile, as shown in Formula (I):

wherein x and y are the molar percentage of 4-vinylphenol and acrylonitrile monomers, respectively, present in the PVPA based polymer, and each can be independently from about 5 to about 95 mole percent, or from about 10 to about 90 mole percent; and n represents repeating units from about 10 to about 10,000. In specific embodiments, the PVPA based polymer is poly(4-vinylphenol-co-acrylonitrile).

The dielectric layer comprises the PVPA based polymer which may have a dielectric constant of from about 3 to about 18. The dielectric constant can be adjusted by controlling the ratio between the two monomers. Generally, the higher the amount of acrylonitrile, the higher the dielectric constant. In further embodiments, the PVPA based polymer has a dielectric constant of from about 4 to about 10. In other embodiments, the molar ratio of 4-vinylphenol to acrylonitrile in the PVPA based polymer is from about 9:1 to about 1:9, or from about 2:1 to about 1:2.

The phenol functional group allows the PVPA based polymer to be crosslinked, photochemically or using crosslinking agents, in the gate dielectric layer. For example, the PVPA based polymer can be photochemically crosslinked under UV irradiation or chemically crosslinked with any suitable crosslinking agent. Exemplary crosslinking agents include melamine-formaldehyde resins (MF-resins), isocyanates, tri(2-aminoethyl)amine, diethylene triamine, formaldehyde-based resins, compounds containing at least two epoxy groups, compounds containing at least two carboxylic acid groups, acid anhydrides of carboxylic acid, and mixtures thereof. In specific embodiments, the gate dielectric layer is crosslinked with MF-resins.

The total thickness of the gate dielectric layer may be, for example, from about 5 nanometers to about 5 microns, including from about 100 nanometers to about 1 micron. In particular embodiments, the gate dielectric layer has a thickness of 2 microns or less, including from about 100 to about 500 nanometers. Unlike other solution processable polymeric gate dielectric materials, the poly(4-vinylphenol-co-acrylonitrile) based polymer does not require a very thin layer in order to achieve low operating voltage. The thicker gate dielectric layer still has good capacitance, low operating voltage, and high charge carrier mobility. The gate dielectric layer may have a conductivity that is, for example, less than about 10⁻¹² Siemens per centimeter (S/cm). When deposited as a film, the dielectric layer will have a large capacitance even with a relatively high thickness. Large capacitance enables low operating voltage, while high thickness warrants low gate leakage. In embodiments, the dielectric layer has a capacitance greater than 5 nF/cm², or greater than 10 nF/cm², preferably greater than 20 nF/cm².

In further embodiments, the gate dielectric layer further comprises inorganic particles such as nanoparticles. The nanoparticles have a particle size of from about 3 nm to about 500 nm, or from about 3 nm to about 100 nm. Any suitable inorganic nanoparticles can be used. Exemplary nanoparticles include metal nanoparticles such as Au, Ag, Cu, Cr, Ni, Pt and Pd; metal oxide nanoparticles such as Al₂O₃, TiO₂, ZrO₂, La₂O₃, Y₂O₃, Ta₂O₅, ZrSiO₄, SrO, SiO, SiO₂, MgO, CaO, HfSiO₄, BaTiO₃, and HfO₂; and other inorganic nanoparticles such as ZnS and Si₃N₄. The addition of inorganic nanoparticles has several advantages. First, the dielectric constant of the overall gate dielectric layer can be increased. Second, when metal nanoparticles are added, the particles can function as electron traps to lower gate leakage of the gate dielectric layer. The inorganic nanoparticles can be from about 0.1% to about 50% or from about 1% to about 20% by weight of the gate dielectric layer.

When a poly(4-vinylphenol-co-acrylonitrile) copolymer is used, it may be synthesized as shown in Formula (II):

Generally, a protected vinylphenol monomer and acrylonitrile (A) are mixed with an initiator to form a polymer (B), which contains a protecting group on the phenol oxygen atom. After hydrolysis of the protecting group, the phenol groups on the polymer chains are produced and thus the poly(vinylphenol-co-acrylonitrile) copolymer (C) is obtained.

The gate dielectric layer is formed using conventional processes known in the art. In embodiments, the gate dielectric layer is formed using liquid depositing techniques. Any suitable liquid depositing technique may be employed. Exemplary liquid depositing techniques include blanket coating such as spin coating, blade coating, rod coating, dip coating, and the like, and printing such as screen printing, ink jet printing, stamping, stencil printing, screen printing, gravure printing, flexography printing, and the like.

The substrate may be composed of materials including but not limited to silicon, glass plate, plastic film or sheet. For structurally flexible devices, plastic substrate, such as for example polyester, polycarbonate, polyimide sheets and the like may be preferred. The thickness of the substrate may be from about 10 micrometers to over 10 millimeters with an exemplary thickness being from about 50 to about 100 micrometers, especially for a flexible plastic substrate and from about 0.5 to about 10 millimeters for a rigid substrate such as glass or silicon.

The gate electrode is composed of an electrically conductive material. It can be a thin metal film, a conducting polymer film, a conducting film made from conducting ink or paste, or the substrate itself, for example heavily doped silicon. Examples of gate electrode materials include but are not restricted to aluminum, gold, silver, chromium, indium tin oxide, conductive polymers such as polystyrene sulfonate-doped poly(3,4-ethylenedioxythiophene) (PSS-PEDOT), and conducting ink/paste comprised of carbon black/graphite. The gate electrode can be prepared by vacuum evaporation, sputtering of metals or conductive metal oxides, conventional lithography and etching, chemical vapor deposition, spin coating, casting or printing, or other deposition processes. The thickness of the gate electrode ranges for example from about 10 to about 200 nanometers for metal films and from about 1 to about 10 micrometers for conductive polymers. Typical materials suitable for use as source and drain electrodes include those of the gate electrode materials such as aluminum, gold, silver, chromium, zinc, indium, conductive metal oxides such as zinc-gallium oxide, indium tin oxide, indium-antimony oxide, conducting polymers and conducting inks. Typical thicknesses of source and drain electrodes are, for example, from about 40 nanometers to about 1 micrometer, including more specific thicknesses of from about 100 to about 400 nanometers.

The semiconducting layer of the present disclosure comprises an organic semiconductor. Regarding electrical performance characteristics, the organic semiconductor usually has a conductivity in the range of 10⁻⁸ to 10⁻⁴ S/cm, preferably from 10⁻⁷ to 10⁻⁵ S/cm. Various dopants known in the art may also be added to change the conductivity. The organic semiconductor can be either a p-type or n-type semiconductor. Examples of organic semiconductors include but are not limited to acenes, such as anthracene, tetracene, pentacene, and substituted pentacenes, perylenes, fullerenes, oligothiophenes, polythiophenes and their substituted derivatives, polypyrrole, poly-p-phenylenes, poly-p-phenylvinylidenes, naphthalenedicarboxylic dianhydrides, naphthalene-bisimides, polynaphthalenes, phthalocyanines such as copper phthalocyanines or zinc phthalocyanines and their substituted derivatives.

In specific embodiments, the organic semiconductors are polythiophenes. Polythiophenes include, for example, regioregular and regiorandom poly(3-alkylthiophene)s, polythiophenes comprising substituted and unsubstituted thienylene groups, polythiophenes comprising optionally substituted thieno[3,2-b]thiophene and/or optionally substituted thieno[2,3-b]thiophene groups, polythiophenes comprising fused-ring aromatic groups, polythiophenes comprising heteroatom-containing fused-ring aromatic groups, and polythiophenes comprising non-thiophene based aromatic groups such as phenylene, fluorene, furan, and the like.

In specific embodiments, the polythiophene semiconductor has the following general structure:

where R and R′ are independently selected from hydrogen, halogen, alkyl, alkoxyalkyl, siloxyalkyl, and perfluoroalkyl; M is a divalent linkage; and n is the number of repeat units. In specific embodiments, M is thienylene, substituted thienylene, bithiophene, terthiophene, arylene, substituted arylene, heteroarylene, or substituted heteroarylene. In more specific embodiments, M is phenylene, thienothiophene, benzothiophene, carbazole, indolocarbazole, fluorene, benzodithiophene, or bithiophene. In other specific embodiments, R and R′ are selected from alkyl. In more specific embodiments, R and R′ are alkyl containing from about 1 to about 25 carbon atoms, including from about 4 to about 18 carbon atoms, and further including from about 6 to about 16 carbon atoms, including isomeric forms thereof, mixtures thereof, and the like.

The semiconducting layer is from about 5 nanometers to about 1000 nanometers deep, including from about 20 to about 100 nanometers in depth. In certain configurations, such as the configurations shown in FIGS. 1 and 4, the semiconducting layer completely covers the source and drain electrodes.

The semiconducting layer can be formed by molecular beam deposition, vacuum evaporation, sublimation, spin-on coating, dip coating, printing (e.g., inkjet printing, screen printing, stencil printing, microcontact printing, flexographic printing), and other conventional processes known in the art, including those processes described in forming the gate electrode.

The various components of the OTFT may be deposited upon the substrate in any order. Generally, however, the gate electrode and the semiconducting layer should both be in contact with the gate dielectric layer. In addition, the source and drain electrodes should both be in contact with the semiconducting layer.

The resulting TFT has good mobility and good current on/off ratio. In embodiments, the TFT may have a charge carrier mobility of 0.01 cm²/V·sec or greater. In other embodiments, the TFT has a current on/off ratio of from about 10⁴ or more.

The following examples are for purposes of further illustrating the present disclosure. The examples are merely illustrative and are not intended to limit devices made in accordance with the disclosure to the materials, conditions, or process parameters set forth therein. All parts are percentages by volume unless otherwise indicated.

EXAMPLES Synthesis of Copolymer

Poly(4-vinyl phenol-co-methacrylonitrile) was synthesized from two monomers by free radical polymerization according to Scheme 1.

To a well stirred solution of 4-tert-butoxystyrene (8.813 g, 50 mmol) and methacrylonitrile (3.354 g, 50 mmol) in 100 ml of 1,4 dioxane, flushed with argon atmosphere, was added an initiator azobisisobutyronitrile (AIBN) (0.12 g, 1 wt %). The reaction mixture was heated to 85° C. and refluxed at this temperature for 24 hours. After the reaction, the mixture was cooled to the room temperature and then precipitated in hexane. After removing solvent, the copolymer of 4-tert-butyoxystyrene and methacrylonitrile (1) was obtained. The final product, poly(4-vinylphenol-co-methacrylonitrile) (2), was obtained by hydrolysis of copolymer (1) in 1,4-dioxane with hydrochloric acid. Mw: 20876; Mn: 14970; Elemental analysis: 0%, 7.66; N %, 5.79. Percentage of methacrylonitrile incorporated in the copolymer calculated from the elemental analysis is 46.3 mol %.

Fabrication of Capacitor and Transistors:

0.08 g of the above copolymer (2) and 0.04 g MF-resin were dissolved in 1 g DMF. After filtration with a 0.2 micrometer PTFE syringe filter, the solution was spin coated onto an aluminum coated PET substrate at 2000 rpm. The aluminum layer functioned as an electrode for the capacitor and transistors. After being dried at 80° C. for about 5-10 minutes, the dielectric layer was crosslinked at 150° C. on a hot plate for about 30 minutes, resulting in a robust layer with a thickness of 300 nm. Gold electrodes were vacuum evaporated on top of the gate dielectric layer to form capacitors. The capacitance was detected to be 11.6 nF/cm² and the dielectric constant was calculated to be 3.9. The above dielectric layer was modified with poly(methyl silsesquioxane) (PMSSQ) interface layer as the follows. The dielectric layer was first plasma cleaned for 30 seconds, followed by washing with water and isopropanol. A dilute solution of PMSSQ in n-butanol was spin coated on top of the gate dielectric layer at 2000 rpm. After being dried at 80° C., the PMSSQ layer was thermally crosslinked at 160° C. for 30 minutes, resulting in a ˜50 nm layer on top of the dielectric layer.

A polythiophene having the following formula was used as the semiconductor:

where n is a number of from about 5 to about 5,000. This polythiophene and its preparation are described in Beng Ong et al., US Patent Application Publication No. US 2003/0160230 A1, the disclosure of which is totally incorporated herein by reference. The polythiophene semiconductor layer was deposited on top of the gate dielectric by spin coating. The semiconductor layer was dried in a vacuum oven at about 80° C. to about 145° C. for 30 minutes, and then cooled down to room temperature. Subsequently, a set of gold source/drain electrode pairs were vacuum evaporated on top of the resulting semiconductor layer through a shadow mask to form a series of thin film transistors with various dimensions. The device showed a mobility of 0.08 cm²/V·s and current on/off ratio of 10⁴-10⁵.

While particular embodiments have been described, alternatives, modifications, variations, improvements, and substantial equivalents that are or may be presently unforeseen may arise to applicants or others skilled in the art. Accordingly, the appended claims as filed and as they may be amended are intended to embrace all such alternatives, modifications variations, improvements, and substantial equivalents. 

1. A thin film transistor comprising a substrate, a gate dielectric layer, and a semiconducting layer, wherein the gate dielectric layer comprises a poly(4-vinylphenol-co-acrylonitrile) based polymer.
 2. The transistor of claim 1, wherein the poly(4-vinylphenol-co-acrylonitrile) based polymer has a dielectric constant of from about 3 to about
 18. 3. The transistor of claim 1, wherein the poly(4-vinylphenol-co-acrylonitrile) based polymer has a dielectric constant of from about 4 to about
 10. 4. The transistor of claim 1, wherein the poly(4-vinylphenol-co-acrylonitrile) based polymer is crosslinked with a crosslinking agent.
 5. The transistor of claim 4, wherein the crosslinking agent is selected from the group consisting of isocyanates, tri(2-aminoethyl)amine, diethylene triamine, melamine-formaldehyde resins, compounds containing at least two epoxy groups, compounds containing at least two carboxylic acid groups, and acid anhydrides of carboxylic acid, and mixtures thereof.
 6. The transistor of claim 1, wherein the molar ratio of 4-vinylphenol to acrylonitrile in the poly(4-vinylphenol-co-acrylonitrile) based polymer is from about 9:1 to about 1:9.
 7. The transistor of claim 1, wherein the molar ratio of 4-vinylphenol to acrylonitrile in the poly(4-vinylphenol-co-acrylonitrile) based polymer is from about 2:1 to about 1:2.
 8. The transistor of claim 1, wherein the poly(4-vinylphenol-co-acrylonitrile) based polymer is a poly(4-vinylphenol-co-acrylonitrile) copolymer.
 9. The transistor of claim 1, wherein the gate dielectric layer further comprises inorganic nanoparticles.
 10. The transistor of claim 1, wherein the gate dielectric layer has a thickness of 2 microns or less.
 11. The transistor of claim 1, wherein the semiconducting layer comprises a thiophene-based polymer.
 12. The transistor of claim 11, wherein the thiophene-base polymer has the structure of formula (1):

where R and R′ are independently selected from hydrogen, halogen, alkyl, alkoxyalkyl, siloxyalkyl, and perfluoroalkyl; M is a divalent linkage; and n is the number of repeat units.
 13. The transistor of claim 1, wherein the gate dielectric layer has a capacitance greater than 5 nF/cm².
 14. The transistor of claim 1, wherein the gate dielectric layer has a thickness of from about 100 nanometers to about 500 nanometers, and a capacitance greater than 5 nF/cm².
 15. A gate dielectric layer for an electronic device, the layer comprising a poly(4-vinylphenol-co-acrylonitrile) based polymer.
 16. A method for preparing a thin-film transistor, comprising: providing a substrate, a gate electrode, a gate dielectric layer, a source electrode, a drain electrode, and a semiconducting layer, wherein the gate dielectric layer comprises a poly(4-vinylphenol-co-acrylonitrile) based polymer; wherein the gate dielectric layer separates the gate electrode from the semiconducting layer, the source electrode, and the drain electrode.
 17. The method of claim 16, wherein the poly(4-vinylphenol-co-acrylonitrile) based polymer is applied by solution deposition.
 18. The method of claim 17, wherein the solution deposition comprises blanket coating, spin coating, blade coating, rod coating, dip coating, printing, screen printing, ink jet printing, stamping, stencil printing, screen printing, gravure printing, and flexography printing.
 19. The method of claim 16, wherein the poly(4-vinylphenol-co-acrylonitrile) based polymer is a poly(4-vinylphenol-co-acrylonitrile) copolymer.
 20. The thin-film transistor formed by the process of claim
 16. 